| Materials of Construction |
| Filter Media: |
amcUltraFlow PES: Pleated single layer of hydrophilic polyethersulfone
amcUltraFlow PES-A: Pleated single layer of proprietary asymmetrical hydrophilic polyethersulfone
amcUltraFlow PP: Pleated multiple layers of hydrophobic melt blown polypropylene
amcUltraFlow PTFE: Pleated single layer of unsupported hydrophobic polytetrafluoroethylene |
| Support Material: |
Polypropylene |
| Structure Components: |
Polypropylene |
| Sealing Technology: |
Thermal bonding |
| |
| Dimensions |
| Nominal Length: |
10 inch (26.0 cm) |
| Diameter: |
83 mm |
| |
| Nominal Pore Size |
amcUltraFlow PES: 0.03, 0.1, 0.2, 0.45, 1.2 µm
amcUltraFlow PES-A: 0.03, 0.1, 0.2, 0.45, 1.2 µm
amcUltraFlow PP: 0.2, 0.45, 1, 3, 5, 10, 30, 60 µm
amcUltraFlow PTFE: 0.05, 0.1, 0.2, 0.45, 1, 5 µm |
| Typical Effective Filtration Area |
amcUltraFlow PES: 1.6 m²/10 inch
amcUltraFlow PES-A: 1.6 m²/10 inch
amcUltraFlow PP: >0.8 m²/10 inch
amcUltraFlow PTFE: 1.7 m²/10 inch |
| |
| Maximum Operating Temperature |
80°C at 30 psi (2.1 bar) |
| |
| Maximum Differential Pressure |
60 psi (4.1 bar) at ambient temperature |
| |
| Resistivity Recovery within 18 Mega-ohm |
≤120 L/10 inch length (at 1 L/min flow rate) |
| |
| Cleanliness |
| amcUltraFlow PES: |
<5 particles/mL (>0.2 µm particle after 5 minutes 18 mΩ water flush at 5 L/min flow rate) |
| amcUltraFlow PES-A: |
<5 particles/mL (>0.2 µm particle after 5 minutes 18 mΩ water flush at 5 L/min flow rate) |
| amcUltraFlow PTFE: |
<10 particles/100 mL (>0.5 µm particle after 30 minutes 18 mΩ water flush at 5 L/min flow rate after alcohol wetting) |
| |
| Retention Efficiency |
| amcUltraFlow PES: |
0.03 μm: >99.9% (retention of 0.055 μm PSL beads)
0.1 μm: >99.999% (retention of 0.198 μm PSL beads)
0.2 μm: >99.999% (retention of 0.460 μm PSL beads)
0.45 μm: >99.9% (retention of 0.830 μm PSL beads)
1.2 μm: >99.99% (retention of 2.0 μm PSL beads) |
| amcUltraFlow PES-A: |
0.03 μm: >99.9% (retention of 0.055 μm PSL beads)
0.1 μm: >99.999% (retention of 0.198 μm PSL beads)
0.2 μm: >99.999% (retention of 0.460 μm PSL beads)
0.45 μm: >99.9% (retention of 0.830 μm PSL beads)
1.2 μm: >99.99% (retention of 2.0 μm PSL beads) |
| amcUltraFlow PP: |
0.2 μm: >99% (retention of 0.3 μm AC fine dust)
0.45 μm: >99% (retention of 0.6 μm AC fine dust)
1 μm: >99% (retention of 1.5 μm AC fine dust)
3 μm: >99% (retention of 5 μm AC fine dust)
5 μm: >99% (retention of 9 μm AC fine dust)
10 μm: >99% (retention of 15 μm AC fine dust)
30 μm: >99% (retention of 40 μm AC fine dust)
60 μm: >99% (retention of 70 μm AC fine dust) |
| Cartridge Configuration |
226/Flat |