Materials of Construction |
Filter Media: |
Pleated non-woven polypropylene |
Support Material: |
Polypropylene |
Structure Components: |
Polypropylene |
Sealing Technology: |
Thermal bonding |
|
Dimensions |
Nominal Length: |
10, 20, 30, and 40 inch (25.4, 50.8, 76.2, and 101.6 cm) |
Diameter: |
2.7 inches (6.9 cm) |
|
Nominal Pore Sizes |
0.2, 0.45, 1, 3, 5, 10, 30, 60 μm |
|
Typical Effective Filtration Area |
0.2, 0.45, 1 μm: 5 ft² (0.5 m²) per 10 inch
3, 5, 10 μm: 6 ft² (0.6 m²) per 10 inch
30, 60 μm: 7 ft² (0.7 m²) per 10 inch |
|
Maximum Operating Temperature |
82°C (180°F) at 10 psi (0.7 bar) |
(Supported adapters are recommended for applications at elevated temperature over 60°C)
|
|
Sterilization/Sanitization Methods |
Autoclave: |
121°C (250°F) for 30 minutes up to 30 cycles |
In-line Steam: |
134°C (273°F) for 60 minutes at3 psi (0.21 bar) maximum differential pressure |
|
Maximum Differential Forward Pressure |
60 psi (4.1 bar) 60 psi (4.1 bar) at ambient temperature |
|
Maximum Differential Back Pressure |
40 psi (2.8 bar) at 60°C (140°F) |
|
Maximum Continuous Pressure |
Limited by housing |
Typical Water Flow Rate (10 inch length)
Typical Air Flow Rates (10 inch length)
0.2 μm Filter Retention Efficiency vs. Particle Size
0.45 μm Filter Retention Efficiency vs. Particle Size
1 μm Filter Retention Efficiency vs. Particle Size
3 μm Filter Retention Efficiency vs. Particle Size
5 μm Filter Retention Efficiency vs. Particle Size
10 μm Filter Retention Efficiency vs. Particle Size
30 μm Filter Retention Efficiency vs. Particle Size
60 μm Filter Retention Efficiency vs. Particle Size