| Materials of Construction |
| Filter Media: |
Pleated hydrophobic PTFE membrane |
| Support Material: |
Polypropylene |
| Structure Components: |
Polypropylene |
| Sealing Technology: |
Thermal bonding |
| |
| Dimensions |
| Nominal Length: |
10, 20, 30 and 40 inch
(25.4, 50.8, 76.2 and 101.6 cm) |
| Diameter: |
2.7 inches (6.9 cm) |
| |
| Nominal Pore Sizes: |
0.1, 0.2 μm |
| |
| Typical Effective Filtration Area5.4 ft² (0.50 m² ) per 10 inch |
| |
| Maximum Operating Temperature90 ℃ (194℉) at 30 psi (2.1 bar)
(Supported adapters are recommended for applications at elevated temperature over 60 ℃)
|
| |
| Sterilization/Sanitization Methods |
| Autoclave: |
121 ℃ (250 ℉) for 30 minutes up to 30 cycles |
| In-line Steam: |
140 ℃ (284 ℉) for 60 minutes at 2 psi (0.14 bar) up to 20 cycles |
| |
| Maximum Differential Forward Pressure |
60 psi (4.1 bar) at ambient temperature |
| |
| Maximum Differential Back Pressure |
15 psi (1.0 bar) at ambient temperature |
| |
| Recommended Integrity Tests |
| |
| Minimum Bubble Point: |
0.1 μm: 21 psi (1.5 bar) - ethanol
0.2 μm: 15 psi (1.1 bar) - ethanol |
| |
| Typical Liquid Flow Rates: |
0.1 μm: 0.6 gpm/psi/10 inch (3 lpm/0.1 bar/25.4 cm）
0.2 μm: 1.1 gpm/psi/10 inch (6 lpm/0.1 bar/25.4 cm） |
| |
| Typical Air Flow Rates: |
0.1 μm: 13 cfm/psi/10 inch at atmospheric pressure (31 Nm³ /hr/0.1 bar/25.4 cm)
0.2 μm: 20 cfm/psi/10 inch at atmospheric pressure (48 Nm³ /hr/0.1 bar/25.4 cm) |
| |
| Typical Non-Volatile Residue |
≤0.01 g /10 inch length in IPA |
| |
| Endotoxin Level |
< 0.25 EU/mL utilizing Limulus Amoebocyte Lysate (LAL) test |
| |
| Membrane materials passes USP Class VI-121 ℃ Plastics Test |
| *For more information, please contact us. |